產(chǎn)品介紹：Teflon? FEP、PFA和Tefzel? ETFE薄膜是透明的熱塑性薄膜，可以通過熱封、熱成型、真空成型、熔融粘接、粘合劑層合、表面金屬化等加工方式與各類材料復合，也可作為熱熔粘合劑。
產(chǎn)品特征：Teflon?/Tefzel?薄膜不僅加工方式多樣，井且具有獨特的性能，這是其它塑料薄膜所無法媲美的。
Teflon? FEP、PFA和Tefcel? ETFE薄膜是透明的熱塑性薄膜，可以通過熱封、熱成型、真空成型、熔融粘接、粘合劑層合、表面金屬化等加工方式與各類材料復合，也可作為熱熔粘合劑。
Teflon?/Tefzel?薄膜不僅加工方式多樣，井且具有獨特的性能，這是其它塑料薄膜所無法媲美的。
| 性質 | ASTM標準 | 單位 | Teflon? FEP 薄膜 | Teflon? PFA薄膜 | Teflon? ETFE 薄膜 | |
| 機械性能 | ||||||
| 拉伸強度 | D882 | MPa | 27 | 27 | 41 | |
| 斷裂伸長率 | D882 | % | 300 | 300 | 100-400 | |
| 拉伸模量 | D882 | MPa | 480 | 480 |
|
|
| 抗沖擊強度 | 杜邦氣動沖擊 測試儀 | J/m | 7.7 X103 | 6.2 X104 | Nobreak | |
| 耐折強度（MIT） | D2176 | MIT | 10,000 | 100,000 | 400,000 | |
| 抗撕裂強度(初始） | D1004 | N/mil | 2.65 | 4.90 | - | |
| 抗撕裂強度(傳遞) | D1922 | N/mil | 1.23 | 0.74 | 2.94 | |
| 破裂強度(Mullen) | D774 | kPa | 76 |
|
- | |
| 熱學性質 | ||||||
| 熔點 | D3418 (DTA) | °C | 260-280 | 302-310 | 250-270 | |
| 導熱系數(shù) | Cenco -Fitch | W/(m.k) | 0.195 | 0.195 | 0.24 | |
| 比熱 | - | J/(kg.k) | 1172 | 1172 | 250 | |
| 尺寸穩(wěn)定性 | 30 分鐘，150°C | % |
MD=0.72 膨脹 TD=2.2收縮 |
MD=1收縮 TD=1收縮 |
md=o收縮 TD=4-7收縮 |
|
| 極限氧指ft | D2863 | % | 95 | 95 |
|
|
| 電學性能 | ||||||
| 介電強度 (23°C 60Hz, 0.025mm) | D149A | kV/mm | 260 | 260 | 160 | |
| 介電常數(shù) (25°C, 100Hz 到 1MHz） | D150 |
|
2.0 | 2.0 | 2.7 | |
| 耗散因子 (25〇C, 100Hz 到 1MHz） | D150 |
|
0.0002 -0.0007 | 0.0002 -0.0007 | 0.0008 | |
| 體積電阻率 (-40°C 到240℃） | D257 | Ohm cm | >lxl018 | >lxl017 | >1 x 1017 | |
| 化學性質 | ||||||
| 吸濕率 | - | % | <0.01 | <0.02 | <0.02 | |
| 氣體滲透率 | D1434 | cm3/(m224 h atm) |
|
|
|
|
| 二氧化碳 |
|
|
25.9 X103 | 14X103 | - | |
| 氮氣 |
|
|
5X103 | 2.0 X103 | - | |
| 氧氣 |
|
|
11.6X103 | 6.7 X103 | - | |
| 蒸汽滲透率 | E96 | g/(m2.d) |
|
|
|
|
| 水 |
|
|
7.0 | 2 | - | |
| 其它性質 | ||||||
| 密度 | D1505 | kg/m3 | 2150 | 2150 | 1730-1770 | |
| 動摩擦系數(shù)(薄膜/鋼） | D1894 |
|
0.1-0.3 | 0.1-0.3 | 0.3-0.5 | |
| 折射率 | D542 |
|
1.341 -1.347 | 1.350 | 1.403 | |
| 太陽光透射率 | E424 | % | 96 | 96 | 94 | |
除特別指明，本表所列數(shù)值為厚度為0.025mm的FEP薄膜和厚度0.050mm的PFA薄膜的性質
1.薄膜種類
FEP, PFA, ETFE
2.薄膜厚度
500相當于5mil,為125微米(lmil=25微米)
3.薄膜的可粘接類型
FEP: A-表面未處理；C-單面可粘；C20-雙面可粘；L-耐環(huán)境應力開裂
PFA: LP-表面未處理；CLP-單面可粘；CLP20-雙面可粘
Tefzel?ETFE: LZ型號-一般類型薄膜；CLZ型號-單面活化處理薄膜；CLZ20型號-雙面可粘
連續(xù)使用溫度范圍：
?FEP： 240-205°C, PFA： 240-260°C, EFTE： 240-150°C
熔點：
?FEP： 250-280°Cf PFA： 300-310°C, ETFE： 250-270°C
?Teflon?樹脂在所有塑料中化學情性最高
?幾乎能抵抗所有化學品的腐蝕
?符合美國食品藥品管理局與食品接觸材料的標準
?各種氣體、液體、蒸汽滲透率低
?高介電強度，厚25 μm 的薄膜介電強度高于260kV/mm
?介電常數(shù)低，并且在很寬的溫度和頻率范圍內(nèi)變化很小
?表面不粘和低摩擦性能
?耐機械沖擊和撕裂
?在低溫下依然可以保持良好物理性能
?非常適于戶外應用，F(xiàn)EP薄膜在佛羅里達州戶外曝曬20年后幾乎無變化
?Teflon?薄膜透光率高達96%,不因陽光暴曬而大幅下降
?Teflon?薄膜不含増塑劑和其它添加劑
?穩(wěn)定的可加工性
?薄膜厚度均勻，無針孔
?Teflon? FEP和PFA氧指數(shù)為95%
?Tefzel? ETFE氧指數(shù)為30%
?光伏封裝前板
?醫(yī)療包裝
?柔性電路板封裝
JIS規(guī)格
| 規(guī)格號碼 | 規(guī)格名稱 |
| JIS K6885 | SEAL用四氟乙烯樹脂生料帶(末加工Tape) |
| JIS K6886 | 四氟乙烯樹脂產(chǎn)品的尺寸 |
| JIS K6887 | 四氟乙烯樹脂 |
| JIS K6888 | 四氟乙烯樹脂板 |
| JIS K6889 | 四氟乙烯樹脂圓形棒 |
| JIS K6890 | 四氟乙烯樹脂管 |
| JIS K6891 | 四氟乙烯樹脂成型粉試驗方法 |
| JIS K6892 | 四氟乙烯樹脂糊狀擠出成型粉試驗方法 |
| JIS K6893 | 四氟乙烯樹脂乳液試驗方法 |
| JIS K6894 | 四氟乙烯樹脂處理涂層(coating |
| JIS K6895 | 四氟乙烯樹脂產(chǎn)品的尺寸測量法 |
| JIS K6896 | 四氟乙烯樹脂成型粉末 |
| JIS K6897 | 四氟乙烯樹脂管 |
ASTM規(guī)格
| Teflon? PTFE樹脂 | ||||||
| 規(guī)格號碼 | 規(guī)格名稱 | |||||
| ASTM D1457 | PTFE Molding and Extrusion Materials | |||||
| ASTM D4894 | PTFE Granular Materials | |||||
| ASTM D4441 | Aqueous dispersions of PTFE | |||||
| ASTM D4895 | PTFE resin produced from dispersion(Fine Powder) | |||||
| ASTM D1710 | PTFE Fluoropolymer Rod | |||||
| ASTM D2571 | PTFE-backed pressure-sensitive electrical insulating tape | |||||
| ASTM D3 293 | PTFE resin molded sheet | |||||
| ASTM D3 294 | PTFE resin molded basic shapes | |||||
| ASTM D3295 | PTFE tubing | |||||
| ASTM D3308 | PTFE resin skived tape | |||||
| ASTM D1000 | Method of testing pressure-sensitive adhesive-coated tapes used forelectrcal insulation | |||||
| ASTM D1895 | Test methods for apparent density, bulk factor and pourability of plastic materials | |||||
| ASTM D1675 | Method fo testing PTFE tubing | |||||
| ASTM D3 297 | Practice for molding and machining tolerance for PTFE resin | |||||
| ASTM D902 | Method of testing flexible resin-coated glass fabrics and glass fabric tapes used for electrical insulation | |||||
| ASTM D3369 | PTFE fluoropolymer resin cast film | |||||
| ASTM F423 | PTFE plastic-lined ferrous metal pipe and fittings | |||||
| Teflon? FEP 樹脂 | ||||||
| 規(guī)格號碼 | 規(guī)格名稱 | |||||
| ASTM D2116 | FEP-Fluoroplymer Molding and Extrusion Materials | |||||
| ASTM D3296 | FEP-Fluoropolymer resin tubing | |||||
| ASTM D3368 | FEP-Fluoropolymer resin sheet and film | |||||
| ASTM F546 | FEP plastic-lined ferrous metal pipe and fittings | |||||
| Teflon? PFA樹脂 | ||||||
| 規(guī)格號碼 | 規(guī)格名稱 | |||||
| ASTM D3307 | PFA-Fluoropolymer Molding and Extrusion Materials | |||||
| ASTM F718 | PFA plastic-lined ferrous metal pipe and fittings | |||||
UL標準
| 規(guī)格號碼 | 規(guī)格名稱 |
| UL-1581 | 200°C Fixture Wire, TefLonTM FEP |
| UL-758 | 150°C and 200°C Appliance Wire； TetlonTMFEP and 250°C TeflonTMFEP PFA/PTFE |
CSA標準
| 規(guī)格號碼 | 規(guī)格名稱 |
| C-22.2No.210 | Appliance Wiring Material； 250°C Teflon? PTFE/PFA, 200°C Teflon? FEP |
| C-22.2No.127 | Equipment Lead Wire； 250°C Teflon?PTFE/PFA( 200°C TeflonTM FEP and 150°C TeflonTM FEP |
Military Specifications
| 規(guī)格號碼 | 規(guī)格名稱 |
| Mil-W-22729/1-12,20-31 | Wire, Electrical, Fluoropolymer insulated Extruded PTFE |
| Mil-W-22729/13,14,15 | Wire, Electrical, Fluoropolymer insulated FEP |
| Mil-C-27500C | Jaketed Materials; Teflon? PFA |
氟化樹脂的現(xiàn)有化學物質名稱整理號碼
| 名稱 | 簡稱 |
現(xiàn)有化學 物質名稱 整思號碼 |
| 四氟乙烯 | PTFE | 6-939 |
| 四氟乙烯共聚合物 | PFA | 6-944 |
| 四氟乙烯?六氟丙烯共聚物 | FEP | 6-946 |
?使用前請務必閱讀產(chǎn)品安全說明書(MSDS)。如需要最新的MSDS,請聯(lián)系您當?shù)氐匿N售代表。
?要加熱至260°C時，一定要安裝排氣裝置，使排氣與換氣充分進行，以避免吸入分解之氣體。
注意事項
?若香煙附著氟塑料時，可能會有吸入分解氣體的危險，因此在使用場所或工作場所一律禁煙，并且禁止攜帶香煙進入。
?使用后，應將衣服上附著的灰塵抖落，手臉洗凈，不要讓氟塑料附著于香煙上。
?本商品并無針對人體移植，或醫(yī)療用途設計生產(chǎn)。
?要廢棄時，一定要依照廢棄物處理及清掃的相關法律進行，絕對不可燃燒。
?不能使用于工作范圍以外。